OKULEN® 2000 is an ultra high molecular low pressure guyenylene with a molecular weight of > 7.000.000 g/mol plus additives for the improvement of specific material properties. It has an antistatic finish and additional lubricant for the conveyor industry. With added antioxidants, for example, which can be used at high temperatures. With additional flame retardant properties for use in rail vehicle, machinery and mining construction. With enhanced antibacterial effects.
Physical Properties | Metric
| English | Comment | |||
Density
| 0.930 g/cc | 0.0336 lb/in³ | ISO 1183-A | |||
|
| |||||
Mechanical Properties | Metric
| English
| Comments
| |||
Hardness, Shore D | 62 | 62 | ISO 868 | |||
Tensile Strength, Yield | >= 17.0 Mpa | >= 2470 psi | ISO/R 527 | |||
Elongation at Break | >= 50.0 % | >= 50.0 % | ISO/R 527 | |||
Creep Strength | 10.0 Mpa | 1450 psi |
| |||
Coefficient of Friction, Dynamic
| 0.0800 | 0.0800 | PE-metal, V = 10 m/min; ASTM D1894 | |||
Coefficient of Friction, Static
| 0.150 | 0.150 | PE-metal, V = 10 m/min; ASTM D1894 | |||
Abrasion | 75.0 | 75.0 | Slurry-Test rel to GUR 4120 = 100%; DIN 58836 Thử bằng hỗn hợp cát+nước theo DIN 58836 | |||
|
| |||||
Electrical Properties
| Metric | English | Comments | |||
Volume Resistivity | <= 1.00e+9 ohm-cm | <= 1.00e+9 ohm-cm | Teil 30; IEC 600093 / VDE 0303 | |||
Thermal Properties | Metric | English |
| |
CTE, linear | 200 µm/m-°C | 111 µin/in-°F |
| |
Melting Point |
| |||
Maximum Service Temperature, Air
| 80.0 °C | 176 °F |
| |
|
| |||
Descriptive Properties |
| |||
Color | Black |
| ||
FDA Approved | No | |||
When the UHMW-PE material meets the specific requirements, OK2000 is usually selected:
• For anti-static and additional lubrication in industrial conveyors
• Add antioxidants to work at high temperatures
• Enhanced bactericidal efficiency in the food industry
OK2000 is also introduced with advanced features, the molecular weight of 6-9 million makes this material more resistant to abrasion while still having the same properties as mentioned above for related applications.